by wilson78

You're absolutely right, need to wait and see what grade they offer first.
If by some stroke of luck they were to offer one of the higher end, US made Madones, then i would be tempted to give it a try.
If not, then like you say it would more than likely be sold to go toward funding another ti, or possibly steel frame. :thumbup:
My Titanium Lemond (RIP):
viewtopic.php?f=10&t=84352" onclick="window.open(this.href);return false;
The Trek:
viewtopic.php?f=10&t=109635

sawyer
Posts: 4485
Joined: Fri Dec 15, 2006 7:45 pm
Location: Natovi Landing

by sawyer

I thought Ti frames never cracked, corroded or degraded and were true "bikes for life"????

LOL, actually I didn't but many Ti devotees wrongly do.

Pleased you found the Ti fault.
----------------------------------------
Stiff, Light, Aero - Pick Three!! :thumbup:

by Weenie


Visit starbike.com Online Retailer for HighEnd cycling components
Great Prices ✓    Broad Selection ✓    Worldwide Delivery ✓

www.starbike.com



User avatar
Valy
Posts: 250
Joined: Tue May 29, 2012 11:16 pm

by Valy

Wow - surely have been lucky here!

Would the bike shop not be able to order a frame via special order via their supplier? Dono if it's different because it's a frame, but I was able to get Speedplays from a shop that normally don't sell them.

dierix
Posts: 27
Joined: Sun Jun 07, 2009 10:51 pm

by dierix

have ridden 2 titanium frames in the past (litespeed and de rosa), both cracked. If I were you I should choose for a stainless steel frame

User avatar
Tinea Pedis
Posts: 8615
Joined: Sat Mar 14, 2009 6:08 am
Contact:

by Tinea Pedis

Like any frame, it's not the material as much the builder which will lead to a frame cracking.

So to say choose stainless as it won't crack is simply wrong.

And those who think their ti bike won't crack might simply be repeating what they were told... (ie: the sales pitch that had them hand over their hard earned).

Wingnut
Posts: 2196
Joined: Sat Jun 23, 2007 12:41 am

by Wingnut

I agree with TP, I could use the same generalisation with carbon frames, steel and aluminum too but don't. Look at the manufacturer first...

franco78_fr
Posts: 12
Joined: Fri Nov 25, 2005 9:33 am

by franco78_fr

I have a 650 Litespeed Vortex and the right base cracked!
it's been repaired by Jean Pierre Levacon in FRANCE and now , it's right !!

picture after:

Image

when repaire by Jean Pierre:

Image

after the repair:

Image

the complete bike :

Image

User avatar
CharlesM
Posts: 5759
Joined: Tue Sep 26, 2006 12:37 am
Location: Phoenix Arizona

by CharlesM

Get the heat / weld wrong and ti will fail... The cracks in this thread are all down to manufacturer error.

Get it right and the fatigue life of ti is generally better than steel or alu of any comparable weight...

ticou
Posts: 459
Joined: Mon Mar 19, 2012 3:31 pm

by ticou

And yet the MpA readings don't lie; 900-1000 for Ti, 1400-2200 for quality steel-reynolds 953 and a USA brand I've forgotten.

User avatar
CharlesM
Posts: 5759
Joined: Tue Sep 26, 2006 12:37 am
Location: Phoenix Arizona

by CharlesM

If you ignore weight and or take things more completely out of cycling context, that would be a good point.

That said, Steel and Alu failures are typically around bad welds too.

sawyer
Posts: 4485
Joined: Fri Dec 15, 2006 7:45 pm
Location: Natovi Landing

by sawyer

CharlesM wrote:Get the heat / weld wrong and ti will fail... The cracks in this thread are all down to manufacturer error.

Get it right and the fatigue life of ti is generally better than steel or alu of any comparable weight...


If that's true it's even more worrying given the brands in this thread include pre-eminent Ti specialists.
----------------------------------------
Stiff, Light, Aero - Pick Three!! :thumbup:

User avatar
CharlesM
Posts: 5759
Joined: Tue Sep 26, 2006 12:37 am
Location: Phoenix Arizona

by CharlesM

I wouldnt worry much about the brands mentioned... They're going to have the odd issue like every other manufacturer.

Of course this is the Internet so if the same failure gets re-reported 100 times, people will claim trek or lite speed have had a hundred failures :lol:

ticou
Posts: 459
Joined: Mon Mar 19, 2012 3:31 pm

by ticou

Well I've only had three failures with Trek, and it was only their cheapo hybrid frames; still, one bike lasted for 3 month's before it cracked. I tend to trek the other way these days, can't think why. Must be the opera.

User avatar
wilson78
Posts: 120
Joined: Mon Jan 11, 2010 10:49 pm

by wilson78

Interesting point there about the pressure values for each material, not what i would have expected.
As for manufacturers, in my situation, as the frame split on the tube i would have to say that it would be Reynolds as the tube maufacturer that were ultimately at fault rather than the frame builder, as there was no problem with any of the welds.
Also, i am pretty sure that i read somewhere that Lemond Ti frames were actually subcontracted to be built by either Lightspeed or Merlin ( can't remember which ) - both as Charles said, well respected Ti frame builders. So it would be rather unfair to hold Trek directly responsible on this occasion. Although depending on how they ultimately respond to the problem i reserve the right to change my opinion!
My Titanium Lemond (RIP):
viewtopic.php?f=10&t=84352" onclick="window.open(this.href);return false;
The Trek:
viewtopic.php?f=10&t=109635

User avatar
CharlesM
Posts: 5759
Joined: Tue Sep 26, 2006 12:37 am
Location: Phoenix Arizona

by CharlesM

understand that a bad weld doesnt mean failing at/on the weld material in most cases.

It more frequently means a failure in the area around the weld or between close welds where heat wasn't properly handled.

The weld material it's self is usually fine but the bad weld damages the thin tube material around it.


Sometimes its the tube material right at the edge of the weld but other times it will be the area at the edge of where the heat changed the structure of the metal... The crack can be a half inch or inch away from the actual weld at the seam where the improperly heated material meets undamaged material (within the same tube).

Other times it will follow a seam or shape / fold away from a weld (like the Litespeed above). It was a mistake welding process that made for the weak spot and or sometimes a poor design like the loads of cracks at poorly engineered gussets on lots of mountain bikes. Sometimes a design requires too many passes or two much jeat concentration.