by WeightySteve

Hey, looking some advice on this before I take the plunge.

The caps that are welded on to the end of the chain stays dont seems to be a structural component of the frame, so is it safe to drill here?

I'm worring about the drill hole spawning cracks along weak points, but I guess even if cracks appear on this end cap, they would stop at the weld joint and not propogate to the chainstay itself. Or would they?

Or maybe to the end caps stop the deformation of the shape chainstays and they are actually an important bit of metal that should not be messed about with?

Any feedback greatly appreciated...

in the industry
Posts: 113
Joined: Sat Nov 17, 2007 4:35 am
Location: Singapore

by soulbike

Technically no problem, but good luck with the drilling through about 4-5mm of titanium....

by Weenie

User avatar
Posts: 2832
Joined: Sat Apr 16, 2005 6:08 pm
Location: Boulder, Colorado

by lancejohnson

That spot is likely fine to drill. It should not be more than 1mm thick or so, use a punch to mark your spot, and then I like to start with a small bit to get a pilot hole in (if you don't have a fixture to hold the frame and the drill/mill this is usually a very good idea), but depending on the size of the hole for Di2/your skill level that may not be necessary.

Good luck.

"Organization is for the simple-minded, the Genius controls the chaos." - Jens

Posts: 417
Joined: Fri Dec 31, 2004 8:43 pm
Location: sweden

by Tim

use a drillstop as well.

User avatar
Posts: 1958
Joined: Fri Mar 23, 2007 12:19 pm
Location: On Pave

by Roobay

Titanium will get very hot get it done professionally, other wise you will find yourself getting through a lot of drill bits :roll:
i like people... i just can't stand assholes

Posts: 37
Joined: Tue Nov 09, 2010 8:02 pm

by mclaren

Just lube the hole often...every 15-20 seconds and your bits will be fine

Posts: 1146
Joined: Fri Jul 17, 2009 4:10 am

by nitropowered

Use a slower speed to drill rather than full rpms. If you have a buddy who can help you, get a sprayer and spray the drilling area with water. Ideally, you would have cutting/cooling solution, but to buy a gallon of that stuff for one simple job is rather pointless.

Posts: 670
Joined: Sat Nov 22, 2008 11:15 pm

by ty-ro

I'd call Litespeed.

User avatar
Posts: 2832
Joined: Sat Apr 16, 2005 6:08 pm
Location: Boulder, Colorado

by lancejohnson

I second the slow speed and water or a spray solution. Just your average spray bottle will work. I've even heard of some builders using windex to cool when cutting. The guys that have suggested that this is a two person job are also pretty spot-on - the area you will be drilling is not going to be conducive to a one-handed job and spraying your cooling solution as you go, so an extra set of hands to squeeze the spray trigger will be very helpful. And if you're not familiar with drilling through metal tubing or something similar, then I definitely recommend the drillstop. As for calling Litespeed, it's insurance, but the info here is solid to cover your bases.

"Organization is for the simple-minded, the Genius controls the chaos." - Jens

Posts: 5068
Joined: Sat Dec 13, 2003 2:25 am
Location: Canada

by Geoff

That should be easy to do for anyone with access to a quality drill press. It might be a pain with hand-held tools, though.

Posts: 1146
Joined: Fri Jul 17, 2009 4:10 am

by nitropowered

how are you going to rig the frame into a drill press? it would be pretty tough to clamp that in there at the correct angle and not damaging the tubes

Shop Wrench
Posts: 284
Joined: Thu Feb 26, 2009 1:18 am
Location: Boston

by RollingGoat

Are there any custom builders in your area who work with titanium? If it was me I'd take it to them and see what they say.
I'm so rubbish at this.

User avatar
Posts: 408
Joined: Sat Aug 23, 2008 5:31 am
Location: Santa Barbara

by Scottybee

If you have ever faced a titanium headtube you will realize what a pain in the ass this is. I would consider taking it to a local machinist- this is one of those "how hard could it be!" situations that end up in something getting destroyed.
17 and stupid, bear with me

User avatar
Posts: 694
Joined: Thu Mar 10, 2005 2:27 pm
Location: Belgium

by $mokeyJoe

If you're familiar with drilling it's a pretty easy job...it's just the material is very hard. Just use the guide explained here above and it should be fine. Drilling that spot won't affect anything. I've a Vortex and it looks almost the same at that point.

But be patient as Ti is very hard! Take your time, new bits beginning with a small hole and work through it to the desired diameter slowly. Spray enough while drilling on slow speed. If it gets too hot, just wait a bit or cool it with a wet rag. Just like drilling a hole but with patience.

I've sanded my Litespeed Vortex...i know how long it takes to work on a surface like Ti...it took me weeks to get my desired look!
*Light is beautiful*
BMC SLC01 5900g ... Litespeed Vortex 6300g ... Merida Carbon Lite 7000g ... Velocite Selene 8000g ... Argon18 E114 +/-8500g ... Trek 1500 9500g

by Weenie

Posts: 7
Joined: Wed Oct 25, 2006 11:50 pm

by decade

How are you going to Di2 the rest of the frame?